PERUBAHAN LAJU KOROSI AKIBAT TEGANGAN DALAM DENGAN METODE C-RING
DOI:
https://doi.org/10.34151/technoscientia.v2i1.423Keywords:
Internal Stress, C-ring, Corrosion, Fastener, Corrosion RateAbstract
Stress Corrosion Craking (SCC) generally attack to metals (steel) under internal stress. Fastener could arised internal stress to material that fastened, such as plat or other material. The experiment to observed SCC could used C-Ring method as standard ASTM G38-01(2007). Fastener and base material that made C-ring corroded in sea water with various stresses that was arrised by fastener. The result of research showed that hardness of spesimen (fastener and C-ring) was increase with increase in stress, the hardness indicated there were internal stress in spesimen. Corrosion rate for spesimen was increase with increase in stress, the higher corrosion rate at spesimen of C-ring for arrised stress 256 kg was 24,20 MPY. and lower arrised stress 69 kg was 19,14 MPY. The spesimen of fastener for arrised stress 256 kg was 7,97 MPY. and lower arrised stress 69 kg was 6,89 MPY. Duration experiment time were 9 day.
References
As’ad, M.A, 2007, Hot Dipping Plat Baja Pada Al Cair Dengan Variasi Waktu Terhadap Ketahanan Korosi Lapisan, Skripsi, Teknik Mesin, Teknologi Industri, Institut Sains Dan Teknologi Akprind Yogyakarta.
Badaruddin, M.S., 2005. Efek Shot Peening Terhadap Korosi Retak Tegang (SCC) Baja Karbon Rendah dalam Lingkungan Air Laut, Jurnal Teknik Mesin, Universitas Kristen Petra Vol 7, no.1 April 2005., hal 11–14.
Fontana, M.G., 1986, Corrosion Engineeing, 3rd edition, McGraw Hill Book Company, New York.
Mamlu, MH, 2001, Penelitian Sifat Fisis Dan Mekanis Pada Besi Beton Yang Mendapat Beban Tekan Dan Dikorosi, Skripsi, Teknik Mesin, Teknologi Industri, Institut Sains Dan Teknologi Akprind Yogyakarta.
Mathari, 2005, Laju Korosi Pada Pengelasan Baja Tahan Karat Similar Dan Dissimilar, Skripsi, Teknik Mesin, Teknologi Industri, Institut Sains Dan Teknologi Akprind Yogyakarta.
Nugroho, RA, 2005, Korosi Pada Baja Paduan Cr (Bohler M300) Yang Mengalami Proses Pemanasan, Skripsi, Teknik Mesin, Teknologi Industri, Institut Sains Dan Teknologi Akprind Yogyakarta.
Sutopo, E, 2001, Pengaruh Media Korosi Pada Kuningan Terhadap Laju Korosi, Kekuatan Tarik, Kekerasan Dan Struktur Mikro, Skripsi, Teknik Mesin, Teknologi Industri, Institut Sains Dan Teknologi Akprind Yogyakarta.
Trethewey, K.R. and Chamberlain J., 1991, Korosi Untuk Mahasiswa Dan Rekayasawan, Gramedia, Jakarta.
Widharto, S., 1999, Karat Dan Pencegahannya, Pradnya Paramita, Jakarta.